1、用扫描电镜对样品或试件进行观察时，样品需要做哪些处理
扫描电镜对样品表面的平整程度要求不高，如果不导电的话需要喷金或者喷碳使其导电即可。
2、扫描电镜样品制备过程中的“喷金”用英语应该怎么说？
Conctive Coating
是涂导电涂料那一步吧，下面是英文的Wiki百科。。找的好苦啊。。。
Conctive Coating – An ultrathin coating of electrically-concting material, deposited either by high vacuum evaporation or by low vacuum sputter coating of the sample. This is done to prevent the accumulation of static electric fields at the specimen e to the electron irradiation required ring imaging. Such coatings include gold, gold/palladium, platinum, tungsten, graphite etc. and are especially important for the study of specimens with the scanning electron microscope. Another reason for coating, even when there is more than enough conctivity, is to improve contrast, a situation more common with the operation of a FESEM (field emission SEM). When an osmium coater is used, a layer far thinner than would be possible with any of the previously mentioned sputtered coatings is possible.[12]
3、金纳米颗粒在做扫描电镜喷金后还能看见吗?
关键看你的金颗粒尺度有多大？如果10nm以下，就很困难，10nm以上，如果不是镶嵌在其他材料中，就可以。SEM 喷金镀膜一般10nm的金晶体可连续成膜，镀膜可复制底层形貌。
4、扫描电镜样品制备过程中的“喷金”用英语应该怎么说
In the process of scanning electron microscopy (sem) sample preparation sprayed gold
5、扫描电镜不导电样品做能谱分析，是喷金还是喷碳好？扫描电镜是钨灯丝的。
喷金比较常见。看你想测试的是啥。。
6、扫描电镜喷金之后是否影响XRD检测
会有影响，应该比较微弱。
XRD使用的光源能量很高，穿透深度一般在毫米级别，而SEM 金膜10nm左右，对于衍射X射线散射率非常低。不影响定性分析，定量影响微乎其微。
7、铝合金阳极氧化膜做扫描电镜需要喷金吗
近几年，扫描电镜发展速度特别快，很多新型扫描电镜因为具有减速电压模式，可以直接拍摄不导电样品，因此无需喷金。因此，题主首先要确认，所用是否有减速电压模式。对于传统电镜，判断是否喷金可以作如下判断：
原理介绍：铝合金阳极氧化膜根据制作工艺和用途的不同，厚度为几纳米到几十微米不等，而电镜电子束打到样品的深度为一到几微米。
1、拍表面：当氧化膜厚度在微米级以下，电子束可以打穿，进入铝合金导电层；厚度在几微米以上，就要喷金处理。
2、拍表面：当只需要放大到几万倍则喷金不影响形貌，当需要放大到几十万甚至几百万倍，则喷金会影响形貌，建议喷白金（Pt）。
3、拍断面：不喷金的话，氧化膜断面很难拍摄清晰。
如果，题主不能判断以上信息，可以不喷金和喷金各放一个，对比拍摄，几乎不会增加工作量，就可以明确了
8、塑料做扫描电镜不喷金或喷碳是不是就得不到清晰的图像
高分子材料必须经过喷金处理后才能用SEM很好的观察。要用SEM看晶体形态结构的话，必须对样品进行刻蚀处理，即把聚合物非晶部分刻蚀掉，结晶部分暴露出来后，才可以在SEM下观察到晶体的形态结构。