1、用掃描電鏡對樣品或試件進行觀察時，樣品需要做哪些處理
掃描電鏡對樣品表面的平整程度要求不高，如果不導電的話需要噴金或者噴碳使其導電即可。
2、掃描電鏡樣品制備過程中的「噴金」用英語應該怎麼說？
Conctive Coating
是塗導電塗料那一步吧，下面是英文的Wiki百科。。找的好苦啊。。。
Conctive Coating – An ultrathin coating of electrically-concting material, deposited either by high vacuum evaporation or by low vacuum sputter coating of the sample. This is done to prevent the accumulation of static electric fields at the specimen e to the electron irradiation required ring imaging. Such coatings include gold, gold/palladium, platinum, tungsten, graphite etc. and are especially important for the study of specimens with the scanning electron microscope. Another reason for coating, even when there is more than enough conctivity, is to improve contrast, a situation more common with the operation of a FESEM (field emission SEM). When an osmium coater is used, a layer far thinner than would be possible with any of the previously mentioned sputtered coatings is possible.[12]
3、金納米顆粒在做掃描電鏡噴金後還能看見嗎?
關鍵看你的金顆粒尺度有多大？如果10nm以下，就很困難，10nm以上，如果不是鑲嵌在其他材料中，就可以。SEM 噴金鍍膜一般10nm的金晶體可連續成膜，鍍膜可復制底層形貌。
4、掃描電鏡樣品制備過程中的「噴金」用英語應該怎麼說
In the process of scanning electron microscopy (sem) sample preparation sprayed gold
5、掃描電鏡不導電樣品做能譜分析，是噴金還是噴碳好？掃描電鏡是鎢燈絲的。
噴金比較常見。看你想測試的是啥。。
6、掃描電鏡噴金之後是否影響XRD檢測
會有影響，應該比較微弱。
XRD使用的光源能量很高，穿透深度一般在毫米級別，而SEM 金膜10nm左右，對於衍射X射線散射率非常低。不影響定性分析，定量影響微乎其微。
7、鋁合金陽極氧化膜做掃描電鏡需要噴金嗎
近幾年，掃描電鏡發展速度特別快，很多新型掃描電鏡因為具有減速電壓模式，可以直接拍攝不導電樣品，因此無需噴金。因此，題主首先要確認，所用是否有減速電壓模式。對於傳統電鏡，判斷是否噴金可以作如下判斷：
原理介紹：鋁合金陽極氧化膜根據製作工藝和用途的不同，厚度為幾納米到幾十微米不等，而電鏡電子束打到樣品的深度為一到幾微米。
1、拍表面：當氧化膜厚度在微米級以下，電子束可以打穿，進入鋁合金導電層；厚度在幾微米以上，就要噴金處理。
2、拍表面：當只需要放大到幾萬倍則噴金不影響形貌，當需要放大到幾十萬甚至幾百萬倍，則噴金會影響形貌，建議噴白金（Pt）。
3、拍斷面：不噴金的話，氧化膜斷面很難拍攝清晰。
如果，題主不能判斷以上信息，可以不噴金和噴金各放一個，對比拍攝，幾乎不會增加工作量，就可以明確了
8、塑料做掃描電鏡不噴金或噴碳是不是就得不到清晰的圖像
高分子材料必須經過噴金處理後才能用SEM很好的觀察。要用SEM看晶體形態結構的話，必須對樣品進行刻蝕處理，即把聚合物非晶部分刻蝕掉，結晶部分暴露出來後，才可以在SEM下觀察到晶體的形態結構。